HALOX® Corrosion Inhibitors
| WATER-BASED SYSTEMS | |||||
| – | FILM THICKNESS | REALIZABLE SALT SPRAY HOURS |
1st RECOMMENDATION |
2nd RECOMMENDATION |
TO IMPROVE ADHESION (SYNERGY) |
| ACRYLIC EMULSION PRIMER |
<15 microns | 100 hours | HALOX® SZP-391 JM 3-5% & HALOX® 550 1-3% |
HALOX® 430 JM 3-5% & HALOX® 550 1-3% |
– |
| >50 microns | 336 hours | HALOX® SZP-391 3-5% | HALOX® 750 3-5% | HALOX® 570 LS or HALOX® 515 1-3% |
|
| >50 microns | 500 hours | HALOX® SZP-391 5% | HALOX® 750 5% | HALOX® 570 LS or HALOX® 515 1-3% |
|
| ACRYLIC ELASTOMERIC COATINGS (ERC) – WHITE |
300-500 microns | 336 hours | HALOX® CW-314 5-8% | HALOX® SZP-391 5-8% | HALOX® 570 LS or HALOX® 515 1-3% |
| ACRYLIC ELASTOMERIC COATINGS (ERC) – PIGMENTED |
300-500 microns | 336 hours | HALOX® CW-314 5-8% | HALOX® SZP-391 5-8% | HALOX® 570 LS or HALOX® 515 1-3% |
| DIRECT-TO-METAL HIGH GLOSS ACRYLIC ENAMEL |
<25 microns | 100 hours | HALOX® SZP-391 JM 1-3% | HALOX® 430 JM 1-3% | HALOX® 570 LS or HALOX® 515 1-3% |
| >25 microns | 336-500 hours | HALOX® SZP-391 3-5% | HALOX® 430 3-5% | HALOX® 570 LS or HALOX® 515 1-3% |
|
| DIRECT-TO-METAL HIGH GLOSS ACRYLIC ENAMEL (Zinc free) |
80-90 microns | 336 hours | HALOX® CW-314 3-5% | HALOX® 430 JM 3-5% | HALOX® 570 LS 1-3% or HALOX® FLASH-X 150® 1% |
| ALKYD EMULSIONS & DISPERSIONS |
<25 microns | 100-200 hours | HALOX® SZP-391 JM 3% & HALOX® 570 LS 1-3% |
HALOX® 430 JM | HALOX® 550 WF or HALOX® 515 1-3% |
| 25-50 microns | 336 hours | HALOX® SZP-391 1-3% & HALOX® 550 WF 1-3% |
HALOX® 750 3-5% | HALOX® 570 LS or HALOX® 515 1-3% |
|
| ALKYD EMULSIONS & DISPERSIONS (Zinc free) |
>50 microns | 500 hours | HALOX® CW-314 2-3% | HALOX® 430 JM 2-3% | HALOX® 570 LS or HALOX® 550 1-3% |
| 2K POLYURETHANE |
<25 microns | 100-200 hours | HALOX® 430 JM 1-3% | HALOX® SZP-391 JM 5% | HALOX® 570 LS 1-3% |
| >25 microns | 336-500 hours | HALOX® 430 3-5% | HALOX® SW-111 3-5% | HALOX® 570 LS 1-3% | |
| 2K EPOXY | <25 microns | 336 hours | HALOX® 430 JM 1-3% | HALOX® SZP-391 JM 1-3% | HALOX® 550 WF 1-3% |
| >25 microns | 500+ hours | HALOX® SW-111 3-5% | HALOX® 430 3-5% | HALOX® 550 WF 1-3% | |
| 2K EPOXY (Zinc free) |
45-50 microns | 1000 (CRS / Bonderite® 952) |
HALOX® CW-314 5-8% | HALOX® SW-111 5-8% | HALOX® 550 WF 1-3% |
| 1K EPOXY | 25+ microns | 68-336 hours | HALOX® 750 5% or HALOX® 550 2% |
HALOX® SW-111 5% | HALOX® 550 WF 1-3% |
| EPOXY DISPERSION |
<25 microns | 336 hours | HALOX® 430 JM 1-3% | HALOX® SZP-391 JM 1-3% | HALOX® 570 LS or HALOX® 515 1-3% |
| >25 microns | 500+ hours | HALOX® SW-111 5-7% | HALOX® 750 5% | HALOX® 570 LS or HALOX® 515 1-3% |
|
| POLYVINYLIDENE CHLORIDE PVDC |
<25 microns | 200 hours | HALOX® SZP-391 JM 1-3% | HALOX® 430 JM 1-3% | HALOX® 550 / 550 WF 1-3% |
| PVDC (Rust Converter Primer) |
<25 microns | 48-168 hours | HALOX® RC-980 | HALOX® 550 WF 3-5% | – |
| CATIONIC ACRYLIC (pH<7) |
>50 microns | 72-100 hours | HALOX® FLASH-X® 330 4-5% Pre-mix (1:1) with Water |
– | HALOX® 550 1-2% |
| CATIONIC ALKYD | >50 microns | 200 hours | HALOX® 550 / 550 WF 1-3% | – | – |
| CATIONIC POLYURETHANE DISPERSIONS |
<50 microns | >200 hours | HALOX® FLASH-X® 330 4-5% Pre-mix (1:1) with Water |
– | HALOX® 550 1-3% |
| ANIONIC POLYURETHANE DISPERSIONS |
>50 microns | <200 hours | HALOX® 430 3-5% | HALOX® 570 LS 1-3% | HALOX® 550 1-3% |
| 1K CATIONIC EPOXY (pH<7) |
>50 microns | 100-500 hours | HALOX® 391 5% | HALOX® 430 JM 5% | HALOX® 550 / 550 WF 1-3% |
| HYBRID ACRYLIC ALKYD |
>50 microns | <200 hours | HALOX® 515 1-3% | HALOX® 570 LS 1-3% | HALOX® 550 / 550 WF 1-3% |
| ACRYLIC EPOXY (Topcoat) |
>50 microns | 500+ hours | HALOX® 570 LS or HALOX® 515 |
HALOX® 550 WF 1-3% | – |
| SILICONE EMULSION |
>50 microns | 200 hours | HALOX® SZP-391 6-8% | HALOX® 570 LS 1-3% | HALOX® 550 WF 1-3% |
| SILICONE ROOF COATINGS |
300-500 microns | 336-500 hours | HALOX® CW-314 5-8% | HALOX® SZP-391 5-8% | HALOX® 570 LS or HALOX® 515 1-3% |
| RUST PREVENTATIVE COATING (Temporary) |
<5 microns | 1-24 hours | HALOX® 550 / 550 WF | – | SEE TDS |
| PHENOLIC DISPERSIONS |
25-50 microns | <500 hours | HALOX® 391 3-5% or HALOX® 550 / 550 WF 1-2% |
HALOX® 750 3-5% | – |
| SOLVENT & OTHER SYSTEMS | |||||
| – | FILM THICKNESS | REALIZABLE SALT SPRAY HOURS |
1st RECOMMENDATION |
2nd RECOMMENDATION |
TO IMPROVE ADHESION (SYNERGY) |
| ACRYLIC EMULSION PRIMER |
25-50 microns | 500 hours | HALOX® SW-111 5-7% | HALOX® 700 5-7% | HALOX® 630 1-3% HALOX® 550 WF 1-4% |
| >50 microns | 1000 hours | HALOX® SW-111 7-10% or HALOX® 550 WF 1-3% |
HALOX® 700 5-7% | HALOX® 630 1-3% | |
| EPOXY ESTER | <25 microns | 336 hours | HALOX® 391 JM 3-5% | HALOX® 430JM 3-5% | HALOX® 550 WF or HALOX® 630 1-3% |
| >25 microns | 500+ hours | HALOX® SZP 391 5-7% | HALOX® 750 5-7% | HALOX® 550 WF or HALOX® 630 1-3% |
|
| ALKYD | <25 microns | 100-200 hours | HALOX® SZP-391 JM 3-5% | HALOX® CW-291 1-3% | HALOX® 550 WF or HALOX® 630 1-3% |
| >25-75 microns | 336-500 hours | HALOX® SZP-391 JM 3-5% & HALOX® CW-2230 (2:1 ratio) 3-5% |
HALOX® SZP-391 3-5% & HALOX® CW-2230 (2:1 ratio) 3-5% |
HALOX® 550 WF 1-3% | |
| ALKYD (Zinc free) |
70-90 microns | 336 hours | HALOX® CW-314 5-8% | HALOX® SZP 391 5-8% | HALOX® 630 or HALOX® 550 WF 0.5-1% |
| 2K POLYURETHANE |
<25 microns | 200 hours | HALOX® 391 JM 1-3% | HALOX® 430 JM 1-3% | HALOX® 550 WF or HALOX® 630 1-3% |
| 25-75 microns | 500+ hours | HALOX® SZP-391 JM 1-3% & HALOX® 550 WF 1-3% | HALOX® 700 3-5% | HALOX® 550 WF 1-3% | |
| MOISTURE CURE POLYURETHANE |
>25 microns | 336 hours | HALOX® CW-2230 3-5% | HALOX® 430 JM 3-5% | HALOX® 550 WF or HALOX® 630 1-3% |
| WASH (Etch) PRIMERS |
<25 microns | 336 hours | HALOX® SZP-391 JM 3-5% & HALOX® 550 WF 1-3% | HALOX® 430 JM 3-5% & HALOX® 550 WF 1-3% |
– |
| COIL COATING POLYESTER |
>25 microns | 500+ hours | HALOX® 430JM 5% & HALOX® 650 0.5% |
HALOX® SZP-391 JM 5% & HALOX® 650 0.5% |
– |
| COIL COATING EPOXY POLYESTER |
<25microns | 500+ hours | HALOX® 430JM 5-8% & HALOX® 650 0.5% |
HALOX® SZP-391 JM 5% & HALOX® 650 0.5% |
– |
| PHENOLIC ALKYD | 25-50 microns | 336 hours | HALOX® SZP-391 6% & HALOX® 550 WF 1% |
HALOX® SZP-391 6% | HALOX® 630 1% |
| ACRYLIC TOPCOAT | 25-50 microns | 200 hours | HALOX® 550 WF 1-3% | HALOX® 630 1-3% | – |
| UV CURE URETHANE OR EPOXY ACRYLATE |
25-50 microns | 500 hours | HALOX® SZP-391 JM 3-5% | HALOX® 570 0.5-2% | HALOX® 550 WF 1-2% |
| POWDER COATING POLYESTER/TGIC |
>25 microns | 500 hours | HALOX® 430 JM 5% | HALOX® CW-314 | HALOX® 650 1-2% |
| POWDER COATING GMA ACRYLIC |
>25 microns | 500+ hours | HALOX® 550 WF 1-3% | HALOX® 430 5-7% | – |
| E-COAT CATHODIC | <25 microns | – | HALOX® 550 WF 1-3% | – | – |
| E-COAT ANODIC | <25 microns | – | HALOX® 550 1-3% | – | – |
| SILICONE (Heat Resistant Coating) |
30-50 microns | <200 hours | HALOX® SZP-391 5-7% | – | HALOX® 550 WF 1-2% |
| ZINC RICH PRIMERS |
20-40 microns | – | HALOX® 550 / 550 WF 2-3% | HALOX® SZP-391 JM 2-6% | – |